Detal Zirconia Disc
Detal Zirconia Disc

Item : CS-2016168-1

Details :

Dental Zirconia Disc block


Using bio-nano zirconia powder as raw material, by isostaic pressing method and deep processing in machining center, our zirconia dental block is obtained.
Our dental zirconia disc blocks have been exported to many countriies including Germany, France, Poland, USA, etc for years.
Our product standard can be also controlled and adjusted according to  the customers' specific requirement.

Available Size(mm)

￠90 X 8mm;   ￠90 X 10mm;   ￠90 X 12mm;   ￠90 X 13.5mm;   ￠90 X 15mm

￠98 X 10mm;  ￠98 X 12mm;  ￠98 X 14mm;    ￠98 X 16mm;    ￠98 X 18mm

￠98 X 20mm;  ￠98 X 22mm;  ￠98 X 24mm;    ￠98 X 26mm;    ￠98 X 28mm

99.5 X 99.5 X 26 mm         75 X 50 X 22 mm      64.5 X 35.5 X 14 mm

99.5 X 99.5 X 22 mm         75 X 50 X 18 mm      64.5 X 35.5 X 18 mm

99.5 X 99.5 X 18 mm         75 X 50 X 16 mm      100 X 100 X 14 mm

99.5 X 99.5 X 16 mm          75 X 50 X 14 mm     100 X 100 X 18 mm

 The raw material, Dental Zirconia Oxide Powder

Zirconia Powder for Medical Dental Technical Data
Type :  Medical Dental (MD-3Y- L)
Application: Medical Dental False Tooth
Technical Index :  
Type ZrO2 （wt%） Stabilizer Primary impurity element SBET（m2/g） lg.los% D50（μm） Sintering density
Y2O （wt%） MgO% SC2O3% Fe2O3 Na2O SiO2 　 　 　 g/cm3
MD-3Y-ZrO2  ≥94.00% 5.20±0.20 / / <30ppm <30ppm <100ppm 13.0-15.0 <0.5 ≤0.5 6.02
1) It is synthesised by Liquid phase coprecipitation process;    
2) The sintering Temperature: 1480℃ and  Sintering density is 6.02 (g/cm3)
3) It is very suitable for dry pressing and the isostatic pressing
 
 
Type :  Medical dental (MDB-3Y-H )
Application: Medical Dental False Tooth
Technical Index :  
Type ZrO2 （wt%） Stabilizer Primary impurity element SBET（m2/g） lg.los% D50（μm） Sintering density
Y2O （wt%） MgO% SC2O3% Fe2O3 Na2O SiO2 　 　 　 g/cm3
MD-3Y-ZrO2  ≥94.00% 5.20±0.20 / / <30ppm <30ppm <100ppm 12.0-13.0 <0.2 ≤0.2 6.08
1) It is synthesised by  Hydrolytic-hydrothermal combination process, 
2) The sintering Temperature: 1480℃ and  Sintering density is 6.08 (g/cm3)
3) It is very suitable for dry pressing and the isostatic pressing